Abstract GdPdCd was obtained in pure form via reaction of the elements in a sealed tantalum tube in a high-frequency furnace. The structure was investigated by X-ray diffraction on both powders and single crystals: ZrNiAl type, P 6 2m , a=758.2(1), c=391.78(7) pm, wR2=0.0410 for 358 F2 values and 14 variables. Striking structural motifs of GdPdCd are two types of palladium-centered tricapped trigonal prisms [Pd1Cd3Gd6] and [Pd2Cd6Gd3]. Together the palladium and cadmium atoms build a three-dimensional network in which the gadolinium atoms fill distorted pentagonal channels. Susceptibility measurements reveal Curie–Weiss behaviour with an effective magnetic moment of 8.2(1) μB/Gd. GdPdCd ord…
Reduction and catalytic behaviour of heterobimetallic copper–lanthanide oxides
2008
Abstract The reduction of the heterobimetallic copper–lanthanide oxides 2CuO·CeO2 and 3CuO·Ln2CuO4 (Ln = La, Pr, Nd) was studied by H2-TG/DTA and H2-TPR. All systems exhibit two main reduction steps accompanied by mass losses in the temperature range 20–1000 °C. The first step was attributed to CuO reduction, whereas the second step is due either to copper reduction in the Ln2CuO4 phase with the concomitant formation of Ln2O3 or to the surface reduction of CeO2. The products were characterized by XRD, SEM, EDX, and BET techniques and are better described as supported copper type materials. They were active for the mesityl oxide (4-methyl-2-penten-2-one) gas phase hydrogenation.